u'amea nikeli TIG ERNiCrMo-3 Mea fa'apipi'i
VAEGA KEMI:
| ALOY(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| GB/T TULAFONO | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.0-4.2 | - | - |
| TULAFONO AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.15-4.15 | 0.02 | 0.015 |
| FA'ATA'ITA'I TAUA | 0.006 | 0.15 | 0.12 | 22.02 | 64.84 | 8.75 | 0.18 | 3.49 | 0.001 | 0.001 |
MESINO MESIN:
| MEATOAGA | MALOSI ALO'O (MPa) | MALOSI FA'ATA'U(MPa) | TULAGA TAUA J/℃ | ELONGATION(%) | ||||
| GB/T TULAFONO | - | - | - | - | ||||
| TULAFONO AWS | - | - | - | - | ||||
| FA'ATA'ITA'I TAUA | - | 790 | 159/-196 | 46 | ||||
Nickel-chromium-molybdenum nickel-base alloy gas uaea uʻamea, o le tuufaatasiga o le 61% Ni-22% Cr-9% Mo-3.5% Nb + Ta.
O u'amea liusuavai e iai mea fa'ainisinia lelei ma lelei le tete'e atu i le pala ma le fa'a'a.
Stable arc, matagofie fausia, tafe lelei o le uʻamea uʻamea, faʻatasi ai ma le faʻatinoina lelei o le faʻagasologa.
VAEGA KEMI:
| ALOY(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| GB/T TULAFONO | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.0-4.2 | - | - |
| TULAFONO AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.15-4.15 | 0.02 | 0.015 |
| FA'ATA'ITA'I TAUA | 0.006 | 0.15 | 0.12 | 22.02 | 64.84 | 8.75 | 0.18 | 3.49 | 0.001 | 0.001 |
MESINO MESIN:
| MEATOAGA | MALOSI ALO'O (MPa) | MALOSI FA'ATA'U(MPa) | TULAGA TAUA J/℃ | ELONGATION(%) | ||||
| GB/T TULAFONO | - | - | - | - | ||||
| TULAFONO AWS | - | - | - | - | ||||
| FA'ATA'ITA'I TAUA | - | 790 | 159/-196 | 46 | ||||
-
u'amea nikeli ENiCrFe-3 Weldin...
-
u'amea nikeli ENiCrMo-6 uelo fa'aeletise tusi ta'iala mo...
-
u'u nikeli fa'aeletise tusi lesona ENiCrFe-2 Weldin...
-
Fa'amea nikeli TIG ERNiCrFe-7A Soldering soldering
-
Fa'amea fa'a nikeli TIG ERNiCr-3 Fa'apipi'i mea fa'aopoopo...
-
u'amea nikeli Eletise ta'iala ENiCrMo-13 weld ...
Tusi lau savali iinei ma lafo mai ia i matou